Abstract

In this study, field test was performed to investigate the strength-improvement effect of shotcrete mixed Micro-silica fume and shotcrete quality was estimated by EFNARC standard. Deterioration test combined the Freezing-thawing and Carbonation was also performed in order to investigate a long-term durability of high-strength shotcrete. As a result of test, the compressive strength of shotcrete using Micro-silica fume was 45.2～55.8MPa and flexible strength was 5.01～6.66MPa, so a promotion ratio of strength was 37～79%, 17～61% respectively. And the strength-improvement effect of strength by silica fume addition ratio of 7.5～10% for cement mass was more superior to the others. Due to relative dynamic modulus, mass decrease rate and carbonation progress of shotcrete mixed Micro-silica fume, it was especially realized that Micro-silica fume reduced deterioration caused by steel fiber and improved a long-term durability of shotcrete.